Beilstein J. Nanotechnol. 2018, 9, 1423–1436, doi:10.3762/bjnano.9.135
Figure 1: SEM images (after barrier layer etching) of a porous alumina membrane (PAM) fabricated using etch t...
Figure 2: SEM surfaces (A, C) and cross-sectional (B, D) views of sample 2 (type I). In the insets – the cont...
Figure 3: SEM images of the back surface of the sample before (A) and after (B) etching the barrier layer on ...
Figure 4: SEM images of the outer (A) and back (B) surfaces and cross-sections (C, D) of the sample (type I) ...
Figure 5: Pore diameter as a function of etching time of a barrier layer for the outer (1) and back (2, 3) su...
Figure 6: Pore diameter as a function of etching time of a barrier layer for PAA formed using the three synth...
Figure 7: SEM images and AFM profiles of the back surface before (A) and after (C) etching of the barrier lay...
Figure 8: Schematic representation of the different models for pore wetting: A – Cassie–Baxter model [38], B – We...
Figure 9: Contact angle as a function of surface topology (middle column images (B, E, H) are outer surfaces ...
Figure 10: Contact angle as a function of surface topology (middle column images (B, E, H) are outer surfaces ...
Figure 11: Contact angle measurements for the outer side of the PAM as a function of pore diameter for various...
Figure 12: Contact angle measurements for the back side of the PAM as a function of pore diameter for various ...
Beilstein J. Nanotechnol. 2016, 7, 1709–1717, doi:10.3762/bjnano.7.163
Figure 1: SEM top view of the obtained porous alumina oxide at different magnification a) 20000×, b) 100000×.
Figure 2: Deposited mass of Ni and of Ni–Fe as a function of the deposition time. Alumina thickness (HPA) is ...
Figure 3: SEM cross-sectional views of the alumina template after galvanostatic dc deposition of Ni–Fe (a, b,...
Figure 4: XRD pattern for Ni NWs in alumina template with HPA of 65 μm and a current density of 3 mA·cm−2, de...
Figure 5: XRD pattern of Ni–Fe NWs inside the alumina template with HPA of 50 μm and a current density 3 mA·cm...
Figure 6: Magnetization as a function of the temperature for Ni NWs fabricated in the alumina template (HPA =...
Figure 7: Magnetization as a function of the temperature for Ni–Fe NWs fabricated in the alumina template (a)...