N₂⁺-implantation-induced tailoring of structural, morphological, optical, and electrical characteristics of sputtered molybdenum thin films

• Usha Rani,
• Kafi Devi,
• Divya Gupta and
• Sanjeev Aggarwal

Beilstein J. Nanotechnol. 2025, 16, 495–509, doi:10.3762/bjnano.16.38

• Usha Rani Kafi Devi Divya Gupta Sanjeev Aggarwal Ion Beam Centre, Department of Physics, Kurukshetra University, Kurukshetra-136119, India 10.3762/bjnano.16.38 Abstract Molybdenum (Mo) thin films have extensive applications in energy storage devices and photovoltaic solar cells because of their

• remarkable thermal stability, high melting point, and chemical inertness. In the present study, Mo thin films of different thicknesses (150, 200, 250, and 300 nm) have been deposited on Si(100) substrates via radio frequency sputtering in an argon atmosphere at room temperature. Some of these films have been

• implanted with 1 × 1017 N2+·cm−2 at 30 keV using a current density of 4 µA·cm−2. Surface morphology and structural, optical, and electrical properties of the as-deposited and implanted Mo thin films have been systematically investigated. The crystallinity of Mo thin films is enhanced with increasing

Electrical and optical enhancement of ITO/Mo bilayer thin films via laser annealing

• Abdelbaki Hacini,
• Ahmad Hadi Ali,
• Nurul Nadia Adnan and
• Nafarizal Nayan

Beilstein J. Nanotechnol. 2022, 13, 1589–1595, doi:10.3762/bjnano.13.133

• structural results show that both the as-deposited and the annealed ITO/Mo thin films have a polycrystalline structure, and that the annealing treatment enhanced the crystallinity of samples. Moreover, the XRD patterns exhibited a cubic structure preferentially oriented along the (222) and (400) planes. The

• energy values of the ITO/Mo thin films were calculated and listed in Table 1. The bandgap energy increased from 2.76 to 2.88 eV, corresponding to 0–120 mJ laser energy. Then it decreased to 2.79 for 240 mJ. This result clearly shows that laser annealing affects significantly the transmittance and the

Optimization of Mo/Cr bilayer back contacts for thin-film solar cells

• Nima Khoshsirat,
• Fawad Ali,
• Vincent Tiing Tiong,
• Mojtaba Amjadipour,
• Hongxia Wang,
• Mahnaz Shafiei and
• Nunzio Motta

Beilstein J. Nanotechnol. 2018, 9, 2700–2707, doi:10.3762/bjnano.9.252

• ; bilayer; chromium; DC sputtering; molybdenum; optical reflectance; Introduction Molybdenum (Mo) thin films are widely used as a back contact for photovoltaic devices such as Cu(In1−xGax)S2 (CIGS) and Cu2ZnSnS4 (CZTS) thin-film solar cells. The back contact is the first layer to be deposited and its